KEATIN® lead-free

KEATIN® SAC0307 NiGe advanced Badlot

KEATIN® SAC0307 NiGe advanced Badlot
KEATIN® SAC0307 NiGe advanced Badlot
  • SAC0307 Bath solder with nickel, germanium and phosphorus special alloy
  • Significantly reduced dross formation up to 93% due to the use of phosphorus
  • Minimal investment and process costs
  • High mechanical reliability of the connection
  • Reduced cracking due to reduced solidification forces
  • Germanium improves the brazing properties as follows:
    - Reduces surface tension i.e. better wetting properties
    - Lowest dross formation, improved tensile strength of the solder joint
    - The germanium content remains stable in the molten solder

Back

Details
Articlenumber Designation Type Weight PU Amount
600-40036-68 KEATIN® SAC0307 NiGe advanced Badlot Sn99Ag0.3Cu0.7 NiGe 0.2 kg triangular bars 20 kg
600-40038-68 KEATIN® SAC0307 NiGe advanced Badlot Sn99Ag0.3Cu0.7 NiGe 1.0 kg ingot 20 kg
600-47109-68 KEATIN® SAC0300 NiGe advanced refill ot Sn99.7Ag0.3 NiGe 0.2 kg triangular bars 20 kg
600-47101-68 KEATIN® SAC0300 NiGe advanced refill ot Sn99.7Ag0.3 NiGe 1.0 kg ingot 20 kg