KEATIN® lead-free

KEATIN® SC07 NiGe advanced Badlot

KEATIN® SC07 NiGe advanced Badlot
KEATIN® SC07 NiGe advanced Badlot
  • SC07 Bad solder with nickel, germanium and phosphorus special alloy
  • Good wetting properties and better passage
  • Fine-grained and glossy surfaces
  • Reduced deposition rates compared to other lead-free solders
  • Significantly reduced dross formation up to 93% due to the use of phosphorus
  • Reduced attack on solder pot and soldering tool
  • Extended service life due to reduced copper enrichment
  • Germanium improves the brazing properties as follows:
    - Reduces surface tension i.e. better wetting properties
    - lowest dross formation, improved tensile strength of the solder joint
    - The germanium content remains stable in the molten solder

Back

Details
Articlenumber Designation Type Weight PU Amount
600-41003-68 KEATIN® SC07 NiGe advanced Badlot Sn99.3Cu0.7 NiGe 0.2 kg triangular bars 20 kg
600-41000-68 KEATIN® SC07 NiGe advanced Badlot Sn99.3Cu0.7 NiGe 1.0 kg ingot 20 kg
600-41002-68 KEATIN® SC02 NiGe advanced refill ot Sn99.8Cu0.2 NiGe 0.2 kg triangular bars 20 kg
600-41001-68 KEATIN® SC02 NiGe advanced refill ot Sn99.8Cu0.2 NiGe 1.0 kg ingot 20 kg